← Products / Heat-shrinkable tubing
Insulation · Identification · Protective sleeving
Heat-Shrinkable Tubing
15 polyolefin heat-shrink tubing series covering halogen-free and red-phosphorus-free, non-flame-retardant, flame-retardant, ultra-thin-wall, high-temperature, high-shrink-ratio, yellow/green identification, low-temperature shrink and dedicated battery/capacitor products.
Browse series and specifications ↓
Select by operating temperature, wall thickness and shrink ratio
Series and specifications
Expand a product to view detailed parameters and complete dimensions.
RSFR-(2X)125HPFHalogen- and Red-Phosphorus-Free Heat-Shrinkable TubingFree of halogens and red phosphorus, for wire insulation and harness protection with higher fire-safety and environmental requirements.
Product introduction
Halogen- and Red-Phosphorus-Free Heat-Shrinkable Tubing is made from irradiation-crosslinked polyolefin. It offers high performance and low-smoke, low-toxicity combustion for wire insulation, solder-joint corrosion protection, mechanical protection and wiring harnesses with demanding fire-safety and environmental requirements. Applications include metro stations, high-speed trains, aircraft and IT/digital-product manufacturing. With no red phosphorus, it does not generate phosphoric acid or phosphine under high-temperature/high-humidity conditions, providing reliable protection as an upgrade for applications using types H and G.
Product features
- Applicable standard: UL224
- Shrink ratio:2:1
- Initial shrink temperature: ≥+80°C
- Full recovery temperature: ≥+125°C
- Operating temperature: -55°C〜+125°C
- Halogen-free and red-phosphorus-free
- Environmental standards:RoHS, IPC/JEDEC-J-STD-709; class H materials
- Standard colors: black, red, yellow, blue, white (other colors on request)
RSFR-(2X)125HPF environmental parameters
| Performance | Parameter | Test method |
|---|---|---|
| Cadmium, Cd; chromium, Cr; mercury, Hg; lead, Pb | Pass if Σ(Cd, Cr, Hg, Pb)≤100; or, if Σ(Cd, Cr, Hg, Pb)≧100, pass only if Σ(Cd, Hg, Pb)≤100 and Cr≤5. | GB/Z21274-2007; GB/Z21275-2007; total chromium according to EPA3052 |
| Bromine, Br (ppm) | ≤900 | Pr EN14582 B |
| Chlorine, Cl (ppm) | ≤900 | Pr EN14582 B |
| Mono- to decabromobiphenyls, PBBs | N/A | GB/Z21276-2007 |
| Mono- to decabromodiphenyl ethers, PBDEs | N/A | GB/Z21276-2007 |
| Red phosphorus (ppm) | ≤1000 | PY-GC/MS |
RSFR-(2X)125HPF product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 158°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 158°CX168h | ≥100 |
| Cold-bend resistance | UL 224(-30°CX1h) | No cracking |
| Flame retardancy | UL 224 | VW-1 |
| Dielectric withstand voltage | UL 224 | 2500 V,1min: no breakdown |
| Dielectric strength (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥1×10¹⁴ |
| Copper corrosion | UL 224(158°CX168h) | No corrosion |
RSFR-(2X)125HPF — 600V halogen-free, red-phosphorus-free flame-retardant heat-shrink tubing (H9 tubing): specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Inner diameter | Wall thickness | ||||
| Φ0.6 | 0.90±0.20 | ≤0.40 | 0.33±0.10 | 200 | 0.50~0.70 |
| Φ0.8 | 1.10±0.20 | ≤0.50 | 0.33±0.10 | 200 | 0.65~0.80 |
| Φ1.0 | 1.50±0.20 | ≤0.65 | 0.36±0.10 | 200 | 0.85~0.90 |
| Φ1.5 | 2.00±0.20 | ≤0.85 | 0.36±0.10 | 200 | 1.00~1.30 |
| Φ2.0 | 2.50±0.20 | ≤1.00 | 0.45±0.10 | 200 | 1.30~1.80 |
| Φ2.5 | 3.00±0.20 | ≤1.30 | 0.45±0.10 | 200 | 1.50~2.30 |
| Φ3.0 | 3.50±0.20 | ≤1.50 | 0.45±0.10 | 200 | 1.80~2.80 |
| Φ3.5 | 4.00±0.20 | ≤1.80 | 0.45±0.10 | 200 | 2.00~3.30 |
| Φ4.0 | 4.70±0.20 | ≤2.00 | 0.45±0.10 | 200 | 2.30~3.80 |
| Φ4.5 | 5.00±0.20 | ≤2.30 | 0.45±0.10 | 100 | 2.50~4.50 |
| Φ5.0 | 5.50±0.20 | ≤2.5 | 0.56±0.10 | 100 | 3.00~4.80 |
| Φ6.0 | 6.50±0.20 | ≤3.0 | 0.56±0.10 | 100 | 3.50~5.30 |
| Φ7 | 7.50±0.30 | ≤3.5 | 0.56±0.10 | 100 | 4.00~6.30 |
| Φ8 | 8.50±0.30 | ≤4.0 | 0.56±0.10 | 100 | 4.50~7.20 |
| Φ9 | 9.50±0.30 | ≤4.5 | 0.56±0.10 | 100 | 5.00~8.20 |
| Φ10 | 10.50±0.30 | ≤5.0 | 0.56±0.10 | 100 | 5.50~9.20 |
| Φ12 | 12.50±0.30 | ≤6.0 | 0.56±0.10 | 100 | 6.50~10.20 |
| Φ14 | 14.50±0.30 | ≤7.0 | 0.70±0.10 | 100 | 7.50~12.20 |
| Φ15 | 15.50±0.40 | ≤7.5 | 0.70±0.15 | 100 | 8.00~14.20 |
| Φ16 | 16.50±0.40 | ≤8.0 | 0.70±0.15 | 100 | 8.50~15.20 |
| Φ18 | 19.00±0.50 | ≤9.0 | 0.70±0.15 | 100 | 10.00~16.10 |
| Φ20 | 22.00±0.50 | ≤10.0 | 0.80±0.15 | 100 | 10.40~18.50 |
| Φ22 | 24.00±0.50 | ≤11.0 | 0.80±0.15 | 100 | 12.50~21.50 |
| Φ25 | 26.00±0.50 | ≤12.5 | 0.90±0.15 | 50 | 14.00~23.50 |
| Φ28 | 29.00±0.50 | ≤14.0 | 0.90±0.15 | 50 | 15.00~25.50 |
| Φ30 | 31.50±1.50 | ≤15.0 | 1.00±0.15 | 50 | 17.50~28.50 |
| Φ35 | 36.50±1.50 | ≤17.5 | 1.00±0.15 | 50 | 20.00~30.00 |
| Φ40 | 41.50±1.50 | ≤20.0 | 1.00±0.15 | 50 | 21.00~35.00 |
RSFR-(2X)125HPF(CB)Ultra-Thin Halogen- and Red-Phosphorus-Free Heat-Shrinkable TubingAn ultra-thin-wall series free of halogens and red phosphorus for miniature component protection and fast shrinking.
Product introduction
Ultra-Thin Halogen- and Red-Phosphorus-Free Heat-Shrinkable Tubing is made from irradiation-crosslinked polyolefin. It offers high performance and low-smoke, low-toxicity combustion for wire insulation, solder-joint corrosion protection, mechanical protection and wiring harnesses with demanding fire-safety and environmental requirements. Applications include metro stations, high-speed trains, aircraft and IT/digital-product manufacturing. With no red phosphorus, it does not generate phosphoric acid or phosphine under high-temperature/high-humidity conditions, providing reliable protection as an upgrade for applications using types H and G.
Product features
- Applicable standard: UL224
- Shrink ratio:2:1
- Initial shrink temperature: ≥+80°C
- Full recovery temperature: ≥+125°C
- Operating temperature: -55°C〜+125°C
- Halogen-free and red-phosphorus-free
- Environmental standards:RoHS, IPC/JEDEC-J-STD-709; class H materials
- Standard colors: black, red, yellow, blue, white (other colors on request)
- Fast shrinking
RSFR-(2X)125HPF(CB) environmental parameters
| Performance | Parameter | Test method |
|---|---|---|
| Cadmium, Cd; chromium, Cr; mercury, Hg; lead, Pb | Pass if Σ(Cd, Cr, Hg, Pb)≤100; or, if Σ(Cd, Cr, Hg, Pb)≧100, pass only if Σ(Cd, Hg, Pb)≤100 and Cr≤5. | GB/Z21274-2007; GB/Z21275-2007; total chromium according to EPA3052 |
| Bromine, Br (ppm) | ≤900 | Pr EN14582 B |
| Chlorine, Cl (ppm) | ≤900 | Pr EN14582 B |
| Mono- to decabromobiphenyls, PBBs | N/A | GB/Z21276-2007 |
| Mono- to decabromodiphenyl ethers, PBDEs | N/A | GB/Z21276-2007 |
| Red phosphorus (ppm) | ≤1000 | PY-GC/MS |
RSFR-(2X)125HPF(CB) product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 158°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 158°CX168h | ≥100 |
| Cold-bend resistance | UL 224(-30°CX1h) | No cracking |
| Flame retardancy | UL 224 | VW-1 |
| Dielectric withstand voltage | UL 224 | 1500 V,1min: no breakdown |
| Dielectric strength (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
| Copper corrosion | UL 224(158°CX168h) | No corrosion |
RSFR-(2X)125HPF(CB) — 300V halogen-free, red-phosphorus-free ultra-thin-wall flame-retardant heat-shrink tubing (H9 tubing): specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Inner diameter | Wall thickness | ||||
| Φ0.6CB | 0.90±0.20 | ≤0.40 | 0.25±0.10 | 200 | 0.50~0.70 |
| Φ0.8CB | 1.10±0.20 | ≤0.50 | 0.25±0.10 | 200 | 0.65~0.80 |
| Φ1.0CB | 1.40±0.20 | ≤0.65 | 0.25±0.10 | 200 | 0.85~1.00 |
| Φ1.5CB | 1.90±0.20 | ≤0.85 | 0.25±0.10 | 200 | 1.00~1.40 |
| Φ2.0CB | 2.40±0.20 | ≤1.00 | 0.28±0.10 | 200 | 1.30~1.80 |
| Φ2.5CB | 2.90±0.20 | ≤1.30 | 0.28±0.10 | 200 | 1.50~2.30 |
| Φ3.0CB | 3.40±0.20 | ≤1.50 | 0.28±0.10 | 200 | 1.80~2.70 |
| Φ3.5CB | 3.90±0.20 | ≤1.80 | 0.25±0.10 | 200 | 2.00~3.20 |
| Φ4.0CB | 4.40±0.20 | ≤2.00 | 0.30±0.10 | 200 | 2.30~3.60 |
| Φ4.5CB | 4.90±0.20 | ≤2.30 | 0.32±0.10 | 100 | 2.50~4.00 |
| Φ5.0CB | 5.50±0.20 | ≤2.5 | 0.32±0.10 | 100 | 3.00~4.50 |
| Φ6.0CB | 6.50±0.20 | ≤3.0 | 0.32±0.10 | 100 | 3.50~5.40 |
| Φ7CB | 7.50±0.30 | ≤3.5 | 0.32±0.10 | 200 | 4.00~6.30 |
| Φ8CB | 8.50±0.30 | ≤4.0 | 0.35±0.10 | 200 | 4.50~7.20 |
| Φ9CB | 9.50±0.30 | ≤4.5 | 0.35±0.10 | 200 | 5.00~8.20 |
| Φ10CB | 10.50±0.30 | ≤5.0 | 0.40±0.10 | 200 | 5.50~9.20 |
| Φ11CB | 11.50±0.30 | ≤5.5 | 0.40±0.10 | 200 | 6.00~10.20 |
| Φ12CB | 12.50±0.30 | ≤6.0 | 0.40±0.10 | 200 | 6.50~11.20 |
| Φ13CB | 13.50±0.30 | ≤6.5 | 0.40±0.10 | 200 | 7.00~12.20 |
| Φ14CB | 14.50±0.30 | ≤7.0 | 0.40±0.10 | 200 | 7.50~13.20 |
| Φ15CB | 15.50±0.40 | ≤7.5 | 0.40±0.10 | 200 | 8.00~14.20 |
| Φ16CB | 16.50±0.40 | ≤8.0 | 0.40±0.10 | 200 | 8.50~15.10 |
| Φ17CB | 17.50±0.40 | ≤8.5 | 0.40±0.10 | 200 | 9.00~16.10 |
| Φ18CB | 18.50±0.40 | ≤9.0 | 0.42±0.10 | 200 | 9.50~17.10 |
| Φ20CB | 20.50±0.50 | ≤10.0 | 0.45±0.10 | 200 | 10.50~18.10 |
| Φ22CB | 22.50±0.50 | ≤11.0 | 0.45±0.10 | 200 | 11.50~20.00 |
| Φ25CB | 25.50±0.50 | ≤12.5 | 0.45±0.10 | 100 | 13.00~22.00 |
RSFR-(2X)105HHalogen-Free Non-Flame-Retardant Heat-Shrinkable Tubing105℃ non-flame-retardant series for insulation and protection of wire harnesses, connectors and consumer electronics.
Product introduction
105°C halogen-free, non-flame-retardant heat-shrink tubing. It is made from irradiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. Its main functions are wire-harness protection, electrical insulation of connectors, rust and corrosion protection of solder joints, and mechanical protection. Its halogen-free, environmentally conscious formulation is widely used in automotive, electronics, consumer goods, decorative and lighting applications.
Product features
- Applicable standard: UL224 CAN/CSA C22.2 NO198.1-99
- Shrink ratio:2:1
- Initial shrink temperature: ≥+70°C
- Full recovery temperature: ≥+105°C
- Operating temperature: -55°C〜+105°C
- Halogen-free, low-smoke, non-toxic, flexible
- Environmental standards:RoHS, IPC/JEDEC-J-STD-709
- Standard colors: clear, black, white, red, yellow, green, blue and other colors, ten international standard colors in total
RSFR-(2X)105H product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Withstand voltage (rated voltage 600V) | UL 224 | 2500 V,1min: no breakdown |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
- Note: other sizes can be customized.
RSFR-(2X)105H dimensional specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Inner diameter | Wall thickness | ||||
| Φ0.5/0.35 | 0.80±0.20 | ≤0.35 | 0.33±0.10 | 400 | 0.4~0.5 |
| Φ0.6/0.40 | 0.90±0.20 | ≤0.40 | 0.33±0.10 | 200 | 0.5~0.7 |
| Φ0.8/0.50 | 1.10±0.20 | ≤0.50 | 0.33±0.10 | 200 | 0.65~0.9 |
| Φ1.0/0.65 | 1.50±0.20 | ≤0.65 | 0.36±0.10 | 200 | 0.85~1.1 |
| Φ1.5/0.85 | 2.00±0.20 | ≤0.85 | 0.36±0.10 | 200 | 1.0~1.3 |
| Φ2.0/1.00 | 2.50±0.20 | ≤1.00 | 0.45±0.10 | 200 | 1.3~1.8 |
| Φ2.5/1.30 | 3.00±0.20 | ≤1.30 | 0.45±0.10 | 200 | 1.5~2.3 |
| Φ3.0/1.50 | 3.50±0.20 | ≤1.50 | 0.45±0.10 | 200 | 1.8~2.8 |
| Φ3.5/1.80 | 4.00±0.20 | ≤1.80 | 0.45±0.10 | 200 | 2.0~3.3 |
| Φ4.0/2.00 | 4.70±0.20 | ≤2.00 | 0.45±0.10 | 200 | 2.5~3.8 |
| Φ4.5/2.30 | 5.00±0.20 | ≤2.30 | 0.45±0.10 | 100 | 2.5~4.0 |
| Φ5.0/2.50 | 5.50±0.20 | ≤2.50 | 0.56±0.10 | 100 | 3.0~4.5 |
| Φ6.0/3.00 | 6.50±0.20 | ≤3.00 | 0.56±0.10 | 100 | 3.5~5.4 |
| Φ7.0/3.50 | 7.50±0.30 | ≤3.50 | 0.56±0.10 | 100 | 4.0~6.3 |
| Φ8.0/4.00 | 8.50±0.30 | ≤4.00 | 0.56±0.10 | 100 | 4.5~7.2 |
| Φ9.0/4.50 | 9.50±0.30 | ≤4.50 | 0.56±0.10 | 100 | 5.0~8.0 |
| Φ10/5.00 | 10.50±0.30 | ≤5.00 | 0.56±0.10 | 100 | 5.5~9.0 |
| Φ11/5.50 | 11.50±0.30 | ≤5.50 | 0.56±0.10 | 100 | 6.0~10 |
| Φ12/6.00 | 12.50±0.30 | ≤6.00 | 0.56±0.10 | 100 | 6.5~11 |
| Φ13/6.50 | 13.50±0.30 | ≤6.50 | 0.70±0.10 | 100 | 6.7~12 |
| Φ14/7.00 | 14.50±0.30 | ≤7.00 | 0.70±0.10 | 100 | 7.5~13 |
| Φ15/7.50 | 15.50±0.40 | ≤7.50 | 0.70±0.10 | 100 | 8.0~14 |
| Φ16/8.00 | 16.50±0.40 | ≤8.00 | 0.70±0.10 | 100 | 8.5~15 |
| Φ17/8.50 | 17.50±0.40 | ≤8.50 | 0.70±0.10 | 100 | 9.0~16 |
| Φ18/9.0 | 19.00±0.50 | ≤9.00 | 0.70±0.10 | 100 | 10.0~17 |
| Φ20/10.0 | 22.00±0.50 | ≤10.0 | 0.80±0.15 | 100 | 11.0~19 |
| Φ22/11.0 | 24.00±0.50 | ≤11.0 | 0.80±0.15 | 100 | 12.5~22 |
| Φ25/12.5 | 26.00±0.50 | ≤12.5 | 0.90±0.15 | 50 | 14~24 |
| Φ28/14.0 | 29.00±0.50 | ≤14.0 | 0.90±0.15 | 50 | 15~29 |
| Φ30/15.0 | 31.50±1.00 | ≤15.0 | 1.00±0.15 | 50 | 17.5~29 |
| Φ35/17.5 | 36.50±1.00 | ≤17.5 | 1.00±0.15 | 50 | 20~30 |
| Φ40/20.0 | 41.50±1.00 | ≤20.0 | 1.00±0.15 | 50 | 22~35 |
| Φ45/22.0 | 46.50±1.50 | ≤22.5 | 1.00±0.20 | 25 | 25~40 |
| Φ50/25.0 | ≥50 | ≤25.0 | 1.10±0.20 | 25 | 28~45 |
- Note: other sizes can be customized.
- Note: other sizes can be customized.
RSFR-(2X)105H(CB)Ultra-Thin Halogen-Free Non-Flame-Retardant Heat-Shrinkable Tubing105℃ non-flame-retardant ultra-thin-wall series for protecting miniature electronic devices and connections.
Product introduction
105°C halogen-free, non-flame-retardant ultra-thin-wall heat-shrink tubing. It is made from irradiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. Its main functions are wire-harness protection, electrical insulation of connectors, rust and corrosion protection of solder joints, and mechanical protection. The ultra-thin wall is especially suitable for protecting miniature electronic devices. It features low-temperature shrinking and a halogen-free, environmentally conscious formulation.
Product features
- Applicable standard: UL224,CAN/CSA C22.2 NO198.1-99
- Shrink ratio:2:1
- Initial shrink temperature: ≥+70°C
- Full recovery temperature: ≥+105°C
- Operating temperature: -55°C〜+105°C
- Halogen-free, low-smoke, non-toxic, flexible
- Environmental standards:RoHS, IPC/JEDEC-J-STD-709
- Standard colors: clear, black, white, red, yellow, green, blue and other colors, ten international standard colors in total
RSFR-(2X)105H(CB) product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Withstand voltage (rated voltage 300V) | UL 224 | 1500 V,1min: no breakdown |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
RSFR-(2X)105H(CB) dimensional specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Inner diameter | Wall thickness | ||||
| Φ0.6CB | 0.90±0.20 | ≤0.40 | 0.20±0.10 | 200 | 0.5~0.7 |
| Φ0.8CB | 1.10±0.20 | ≤0.50 | 0.20±0.10 | 200 | 0.6~0.9 |
| Φ1.0CB | 1.40±0.20 | ≤0.65 | 0.20±0.10 | 200 | 0.85~1.1 |
| Φ1.5CB | 1.90±0.20 | ≤0.85 | 0.20±0.10 | 200 | 1.0~1.5 |
| Φ2.0CB | 2.40±0.20 | ≤1.00 | 0.22±0.10 | 200 | 1.3~2.0 |
| Φ2.5CB | 2.90±0.20 | ≤1.30 | 0.25±0.10 | 200 | 1.5~2.5 |
| Φ3.0CB | 3.40±0.20 | ≤1.50 | 0.28±0.10 | 200 | 1.8~3.0 |
| Φ3.5CB | 3.90±0.20 | ≤1.80 | 0.28±0.10 | 200 | 2.0~3.5 |
| Φ4.0CB | 4.40±0.20 | ≤2.00 | 0.30±0.10 | 200 | 2.3~4.0 |
| Φ4.5CB | 4.90±0.20 | ≤2.30 | 0.30±0.10 | 100 | 2.5~4.5 |
| Φ5.0CB | 5.50±0.20 | ≤2.50 | 0.32±0.10 | 100 | 3.0~5.0 |
| Φ6.0CB | 6.50±0.20 | ≤3.00 | 0.32±0.10 | 100 | 3.5~5.5 |
| Φ7CB | 7.50±0.30 | ≤3.50 | 0.32±0.10 | 200 | 4.0~6.5 |
| Φ8CB | 8.50±0.30 | ≤4.00 | 0.32±0.10 | 200 | 4.5~7.5 |
| Φ9CB | 9.50±0.30 | ≤4.50 | 0.35±0.10 | 200 | 5.0~8.5 |
| Φ10CB | 10.50±0.30 | ≤5.00 | 0.35±0.10 | 200 | 5.5~9.5 |
| Φ11CB | 11.50±0.30 | ≤5.50 | 0.40±0.10 | 200 | 6.0~10.5 |
| Φ12CB | 12.50±0.30 | ≤6.00 | 0.40±0.10 | 200 | 6.5~11.5 |
| Φ13CB | 13.50±0.30 | ≤6.50 | 0.40±0.10 | 200 | 7.0~12.5 |
| Φ14CB | 14.50±0.30 | ≤7.00 | 0.40±0.10 | 200 | 7.5~13.5 |
| Φ15CB | 15.50±0.40 | ≤7.50 | 0.40±0.10 | 200 | 8.0~14.5 |
| Φ16CB | 16.50±0.40 | ≤8.00 | 0.40±0.10 | 200 | 8.5~15.5 |
| Φ17CB | 17.50±0.40 | ≤8.50 | 0.40±0.10 | 200 | 9.0~16.5 |
| Φ18CB | 18.50±0.40 | ≤9.00 | 0.42±0.10 | 200 | 10.0~17.5 |
| Φ20CB | 20.50±0.50 | ≤10.0 | 0.45±0.10 | 200 | 11.0~18.5 |
| Φ22CB | 22.50±0.50 | ≤11.0 | 0.45±0.10 | 200 | 12.5~20.5 |
| Φ25CB | 25.50±0.50 | ≤12.5 | 0.45±0.10 | 100 | 14.0~22.5 |
RSFR-(2X)125HHalogen-Free Flame-Retardant Heat-Shrinkable Tubing125℃ halogen-free, flame-retardant series for electronic components, automotive wire harnesses and communications applications.
Product introduction
125°C halogen-free, environmentally conscious flame-retardant heat-shrink tubing. It is made from irradiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. Its main functions are wire-harness protection, electrical insulation of connectors, rust and corrosion protection of solder joints, and mechanical protection. It is halogen-free and environmentally conscious, with flame-retardant properties, and is widely used for automotive wire harnesses, electronic components and communications.
Product features
- Applicable standard: UL224,CAN/CSA C22.2 NO198.1-99
- Shrink ratio:2:1
- Initial shrink temperature: ≥+84°C
- Full recovery temperature: ≥+125°C
- Operating temperature: -55°C〜+125°C
- Halogen-free, non-toxic, flexible, flame-retardant
- Environmental standards:RoHS, IPC/JEDEC-J-STD-709; class H materials
- Standard colors: black, red, green, blue and other colors, ten international standard colors in total
RSFR-(2X)125H product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 158°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 158°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Flame retardancy | ASTM D 2671 Method C | VW-1 |
| Withstand voltage (rated voltage 600V) | UL 224 | 2500 V,1min: no breakdown |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
- Note: Sizes Φ30 and above are supplied as type G by default (environmental performance complies with EU RoHS2.0 (2011/65/EU)). Specify type H halogen-free heat-shrinkable tubing on the order if required.
RSFR-(2X)125H dimensional specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Inner diameter | Wall thickness | ||||
| Φ0.5/0.35 | 0.80±0.20 | ≤0.35 | 0.33±0.10 | 400 | 0.3~0.6 |
| Φ0.6/0.40 | 0.90±0.20 | ≤0.40 | 0.33±0.10 | 400 | 0.4~0.7 |
| Φ0.8/0.50 | 1.10±0.20 | ≤0.50 | 0.33±0.10 | 400 | 0.6~0.8 |
| Φ1.0/0.65 | 1.50±0.20 | ≤0.65 | 0.36±0.10 | 400 | 0.75~0.9 |
| Φ1.5/0.85 | 2.00±0.20 | ≤0.85 | 0.36±0.10 | 400 | 0.95~1.4 |
| Φ2.0/1.00 | 2.50±0.20 | ≤1.00 | 0.45±0.10 | 400 | 1.1~1.8 |
| Φ2.5/1.30 | 3.00±0.20 | ≤1.30 | 0.45±0.10 | 400 | 1.35~2.3 |
| Φ3.0/1.50 | 3.50±0.20 | ≤1.50 | 0.45±0.10 | 400 | 1.6~2.7 |
| Φ3.5/1.80 | 4.00±0.20 | ≤1.80 | 0.45±0.10 | 400 | 1.85~3.2 |
| Φ4.0/2.00 | 4.70±0.20 | ≤2.00 | 0.45±0.10 | 400 | 2.1~3.6 |
| Φ4.5/2.30 | 5.00±0.20 | ≤2.30 | 0.56±0.10 | 200 | 2.35~4.0 |
| Φ5.0/2.50 | 5.50±0.20 | ≤2.50 | 0.56±0.10 | 200 | 2.6~4.5 |
| Φ5.5/2.75 | 6.00±0.20 | ≤2.75 | 0.56±0.10 | 200 | 2.9~5.0 |
| Φ6.0/3.00 | 6.50±0.20 | ≤3.00 | 0.56±0.10 | 200 | 3.1~5.4 |
| Φ7.0/3.50 | 7.50±0.30 | ≤3.50 | 0.56±0.10 | 100 | 3.7~6.3 |
| Φ8.0/4.00 | 8.50±0.30 | ≤4.00 | 0.56±0.10 | 100 | 4.2~7.2 |
| Φ9.0/4.50 | 9.50±0.30 | ≤4.50 | 0.56±0.10 | 100 | 4.7~8.0 |
| Φ10.0/5.00 | 10.50±0.30 | ≤5.00 | 0.56±0.10 | 100 | 5.2~9.0 |
| Φ11.0/5.50 | 11.50±0.30 | ≤5.50 | 0.56±0.10 | 100 | 5.7~10 |
| Φ12.0/6.00 | 12.50±0.30 | ≤6.00 | 0.56±0.10 | 100 | 6.2~11 |
| Φ13.0/6.50 | 13.50±0.30 | ≤6.50 | 0.70±0.10 | 100 | 6.7~12 |
| Φ14.0/7.00 | 14.50±0.30 | ≤7.00 | 0.70±0.10 | 100 | 7.3~13 |
| Φ15.0/7.50 | 15.50±0.40 | ≤7.50 | 0.70±0.10 | 100 | 7.8~14 |
| Φ16,0/8.00 | 16.5±0.4 | ≤8.00 | 0.70±0.10 | 100 | 8.3~15 |
| Φ17/8.50 | 17.5±0.4 | ≤8.50 | 0.70±0.10 | 100 | 8.8~16 |
| Φ18/9.00 | 19.0±0.5 | ≤9.00 | 0.70±0.10 | 100 | 9.3~17 |
| Φ20/10.0 | 22.0±0.5 | ≤10.0 | 0.80±0.15 | 100 | 10.5~19 |
| Φ22/11.0 | 24.0±0.5 | ≤11.0 | 0.80±0.15 | 100 | 11.4~21 |
| Φ25/12.5 | 26.0±0.5 | ≤12.5 | 0.90±0.15 | 50 | 12.8~24 |
| Φ28/14.0 | 29.0±0.5 | ≤14.0 | 0.90±0.15 | 50 | 14.4~29 |
| Φ30/15.0 | 31.5±1.0 | ≤15.0 | 1.00±0.15 | 50 | 16~29 |
| Φ35/17.5 | 36.5±1.0 | ≤17.5 | 1.00±0.15 | 50 | 18~34 |
| Φ40/20.0 | 41.5±1.0 | ≤20.0 | 1.00±0.15 | 50 | 21~35.0 |
| Φ45/22.0 | 46.5±1.5 | ≤22.5 | 1.00±0.20 | 25 | 23.5~44 |
| Φ50/25.0 | ≥50.0 | ≤25.0 | 1.10±0.20 | 25 | 26~49 |
| Φ60/35.0 | ≥60.0 | ≤30.0 | 1.20±0.15 | 25 | 35~50 |
| Φ70/35.0 | ≥70.0 | ≤35.0 | 1.30±0.20 | 25 | 40~60 |
| Φ80/40.0 | ≥80.0 | ≤40.0 | 1.30±0.20 | 25 | 45~70 |
| Φ90/45.0 | ≥90.0 | ≤45.5 | 1.30±0.20 | 25 | 50~80 |
| Φ100/50.0 | ≥100.0 | ≤50.0 | 1.30±0.20 | 25 | 55~85 |
| Φ120/60.0 | ≥120.0 | ≤60.0 | 1.30±0.20 | 25 | 65~100 |
| Φ150/75.0 | ≥150.0 | ≤75.0 | 1.30±0.20 | 25 | 80~120 |
| Φ180/90.0 | ≥180.0 | ≤90.0 | 1.30±0.30 | 25 | 85~150 |
| Φ210/105.0 | ≥210.0 | ≤105.0 | 1.30±0.30 | 25 | 110~180 |
| Φ230/115.0 | ≥230.0 | ≤115.0 | 1.30±0.30 | 25 | 120~210 |
| Φ250/125.0 | ≥250.0 | ≤125.0 | 1.30±0.30 | 25 | 130~230 |
| Φ300/150.0 | ≥300.0 | ≤150 | 1.30±0.30 | 25 | 160~250 |
- Note: Sizes Φ30 and above are supplied as type G by default (environmental performance complies with EU RoHS2.0 (2011/65/EU)). Specify type H halogen-free heat-shrinkable tubing on the order if required.
- Note: Sizes Φ30 and above are supplied as type G by default (environmental performance complies with EU RoHS2.0 (2011/65/EU)). Specify type H halogen-free heat-shrinkable tubing on the order if required.
RSFR-(2X)125H(CB)Ultra-Thin Halogen-Free Flame-Retardant Heat-Shrinkable Tubing125℃ halogen-free, ultra-thin-wall, flame-retardant series for miniature devices with specific covering-thickness requirements.
Product introduction
125°C halogen-free, ultra-thin-wall flame-retardant heat-shrink tubing. It is made from irradiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. Its main functions are wire-harness protection, electrical insulation of connectors, rust and corrosion protection of solder joints, and mechanical protection. The ultra-thin wall is particularly suitable for protecting miniature electronic devices. The halogen-free formulation and flame-retardant performance have been improved to meet a wider range of customer requirements.
Product features
- Applicable standard: UL224,CAN/CSA C22.2 NO198.1-99
- Shrink ratio:2:1
- Initial shrink temperature: ≥+70°C
- Full recovery temperature: ≥+110°C
- Operating temperature: -55°C〜+125°C
- Halogen-free, flexible, flame-retardant, fast-shrinking
- Environmental standards:RoHS, IPC/JEDEC-J-STD-709; class H materials
- Standard colors: black, red, green, blue and other colors, ten international standard colors in total
RSFR-(2X)125H(CB) product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 158°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 158°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Flame retardancy | ASTM D 2671 Method C | VW-1 |
| Withstand voltage (rated voltage 300V) | UL 224 | 1500 V,1min: no breakdown |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
RSFR-(2X)125H(CB) dimensional specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Inner diameter | Wall thickness | ||||
| Φ0.6CB | 0.90±0.20 | ≤0.40 | 0.20±0.10 | 200 | 0.4~0.7 |
| Φ0.8CB | 1.10±0.20 | ≤0.50 | 0.20±0.10 | 200 | 0.6~0.8 |
| Φ1.0CB | 1.40±0.20 | ≤0.65 | 0.20±0.10 | 200 | 0.7~1.0 |
| Φ1.5CB | 1.90±0.20 | ≤0.85 | 0.20±0.10 | 200 | 0.9~1.4 |
| Φ2.0CB | 2.40±0.20 | ≤1.00 | 0.22±0.10 | 200 | 1.1~1.8 |
| Φ2.5CB | 2.90±0.20 | ≤1.30 | 0.25±0.10 | 200 | 1.4~2.3 |
| Φ3.0CB | 3.40±0.20 | ≤1.50 | 0.28±0.10 | 200 | 1.6~2.7 |
| Φ3.5CB | 3.90±0.20 | ≤1.80 | 0.28±0.10 | 200 | 1.9~3.2 |
| Φ4.0CB | 4.40±0.20 | ≤2.00 | 0.30±0.10 | 200 | 2.1~3.6 |
| Φ4.5CB | 4.90±0.20 | ≤2.30 | 0.30±0.10 | 100 | 2.4~4.0 |
| Φ5.0CB | 5.50±0.20 | ≤2.50 | 0.32±0.10 | 100 | 2.6~4.5 |
| Φ6.0CB | 6.50±0.20 | ≤3.00 | 0.32±0.10 | 100 | 3.1~5.4 |
| Φ7.0CB | 7.50±0.30 | ≤3.50 | 0.32±0.10 | 200 | 3.7~6.3 |
| Φ8.0CB | 8.50±0.30 | ≤4.00 | 0.32±0.10 | 200 | 4.2~7.2 |
| Φ9.0CB | 9.50±0.30 | ≤4.50 | 0.35±0.10 | 200 | 4.7~8.0 |
| Φ10CB | 10.50±0.30 | ≤5.00 | 0.35±0.10 | 200 | 5.2~9.0 |
| Φ11CB | 11.50±0.30 | ≤5.50 | 0.40±0.10 | 200 | 5.8~10.0 |
| Φ12CB | 12.50±0.30 | ≤6.00 | 0.40±0.10 | 200 | 6.2~11.0 |
| Φ13CB | 13.50±0.30 | ≤6.50 | 0.40±0.10 | 200 | 6.7~12.0 |
| Φ14CB | 14.50±0.30 | ≤7.00 | 0.40±0.10 | 200 | 7.3~13.0 |
| Φ15CB | 15.50±0.40 | ≤7.50 | 0.40±0.10 | 200 | 7.8~14.0 |
| Φ16CB | 16.50±0.40 | ≤8.00 | 0.40±0.10 | 200 | 8.3~15.8 |
| Φ17CB | 17.50±0.40 | ≤8.50 | 0.40±0.10 | 200 | 8.8~16.0 |
| Φ18CB | 18.50±0.50 | ≤9.00 | 0.42±0.10 | 200 | 9.3~17.0 |
| Φ20CB | 20.50±0.50 | ≤10.0 | 0.45±0.10 | 200 | 10.5~19.0 |
| Φ22CB | 22.50±0.50 | ≤11.0 | 0.45±0.10 | 200 | 11.5~20.5 |
| Φ25CB | 25.50±0.50 | ≤12.5 | 0.45±0.10 | 100 | 13.0~24.0 |
| Φ28CB | 28.50±0.50 | ≤14.0 | 0.60±0.10 | 100 | 14.5~27.0 |
RSFR-(2X)150HHalogen-Free High-Temperature Flame-Retardant Heat-Shrinkable TubingOperating temperature up to 150℃, for insulation protection of wire harnesses and connectors in high-temperature environments.
Product introduction
Halogen-free high-temperature flame-retardant tubing is made from irradiation-crosslinked polyolefin. Flame-retardant, heat-resistant and free of halogens and antimony, it offers excellent physical, chemical and electrical properties. It provides connector insulation in hot environments, solder-joint corrosion protection, mechanical protection and harness protection in electronics, communications, automotive, shipbuilding and aircraft manufacturing, especially household aroma heaters, induction cookers, rice cookers, microwave ovens and ovens.
Product features
- Applicable standards: UL224, CAN/CSA C22.2 NO198.1-99, AMS-DTL-23053/5 class 1
- Shrink ratio:2:1
- Initial shrink temperature: ≥+84°C
- Full recovery temperature: ≥+135°C
- Operating temperature: -55°C〜+150°C
- Good elasticity, low smoke, flexible, flame retardant
- Environmental standards:RoHS
- Standard colors: black, white, red, yellow, green, blue and other colors, ten international standard colors in total
RSFR-(2X)150H product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 180°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 180°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Flame retardancy | ASTM D 2671 Method C | VW-1 |
| Withstand voltage (rated voltage 600V) | UL 224 | 2500V,1min: no breakdown |
| Thermal shock | UL224(250°CX4h) | No cracking or dripping |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
RSFR-(2X)150H dimensional specifications
| Size mm | Dimensions before shrinkage mm — inner diameter | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Maximum inner diameter | Wall thickness | ||||
| Φ1.0 | 1.5±0.2 | ≤0.65 | 0.38±0.10 | 200 | 0.75〜1.00 |
| Φ1.5 | 2.0±0.2 | ≤0.85 | 0.40±0.10 | 200 | 0.95〜1.40 |
| Φ2.0 | 2.5±0.2 | ≤1.00 | 0.44±0.10 | 200 | 1.10〜1.80 |
| Φ2.5 | 3.0±0.2 | ≤1.25 | 0.44±0.10 | 200 | 1.40〜2.20 |
| Φ3.0 | 3.5±0.2 | ≤1.50 | 0.44±0.10 | 200 | 1.65〜2.60 |
| Φ3.5 | 4.0±0.2 | ≤1.75 | 0.44±0.10 | 200 | 1.95〜3.00 |
| Φ4.0 | 4.5±0.2 | ≤2.00 | 0.44±0.10 | 200 | 2.20〜3.40 |
| Φ4.5 | 5.0±0.2 | ≤2.25 | 0.44±0.10 | 100 | 2.50〜3.80 |
| Φ5.0 | 5.5±0.2 | ≤2.50 | 0.56±0.10 | 100 | 2.80〜4.20 |
| Φ6.0 | 6.5±0.2 | ≤3.00 | 0.56±0.10 | 100 | 3.30〜5.00 |
| Φ7.0 | 7.5±0.3 | ≤3.50 | 0.56±0.15 | 100 | 3.90〜5.75 |
| Φ8.0 | 8.5±0.3 | ≤4.00 | 0.56±0.15 | 100 | 4.40〜6.50 |
| Φ9.0 | 9.5±0.3 | ≤4.50 | 0.56±0.15 | 100 | 5.00〜7.30 |
| Φ10 | 10.5±0.3 | ≤5.00 | 0.56±0.15 | 100 | 5.50〜8.10 |
| Φ11 | 11.5±0.3 | ≤5.50 | 0.56±0.15 | 100 | 6.10〜8.90 |
| Φ12 | 12.5±0.4 | ≤6.00 | 0.56±0.15 | 100 | 6.60〜9.60 |
| Φ13 | 13.5±0.4 | ≤6.50 | 0.69±0.15 | 100 | 7.20〜10.40 |
| Φ14 | 14.5±0.4 | ≤7.00 | 0.69±0.15 | 100 | 7.70〜11.20 |
| Φ15 | 15.5±0.4 | ≤7.50 | 0.69±0.15 | 100 | 8.30〜12.00 |
| Φ16 | 16.5±0.4 | ≤8.00 | 0.69±0.15 | 100 | 8.80〜12.80 |
| Φ17 | 17.5±0.4 | ≤8.50 | 0.69±0.15 | 100 | 9.40〜13.60 |
| Φ18 | 19.2±0.5 | ≤9.00 | 0.77±0.15 | 100 | 9.90〜14.90 |
| Φ20 | 22.0±0.5 | ≤10.0 | 0.77±0.15 | 100 | 11.00〜17.20 |
| Φ22 | 24.0±0.6 | ≤11.0 | 0.77±0.15 | 100 | 12.10〜18.70 |
| Φ25 | 26.0±0.6 | ≤12.5 | 0.87±0.20 | 50 | 13.80〜20.30 |
| Φ28 | 29.0±0.6 | ≤14.0 | 0.87±0.20 | 50 | 15.40〜22.70 |
RSFR-(2X)125GFlame-retardant heat-shrink tubing125℃ flame-retardant series for wire-harness protection, connector insulation and mechanical protection.
Product introduction
125°C flame-retardant heat-shrink tubing. It is made from irradiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. Its main functions are wire-harness protection, electrical insulation of connectors, rust and corrosion protection of solder joints, and mechanical protection. Its flame-retardant properties help protect lines and components. It is widely used in automotive component protection, shipbuilding and aircraft manufacturing.
Product features
- Applicable standard: UL224,CAN/CSA C22.2 NO198.1-99
- Shrink ratio:2:1
- Flame-retardant, environmentally friendly
- Initial shrink temperature: ≥+84°C
- Full recovery temperature: ≥+125°C
- Operating temperature: -55°C〜+125°C
- Environmental standards:RoHS
- Standard colors: black, white, red, yellow, green, blue and other colors, ten international standard colors in total
RSFR-(2X)125G product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 158°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 158°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Flame retardancy | ASTM D 2671 Method C | VW-1 |
| Withstand voltage (rated voltage 600V) | UL 224 | 2500V,1min: no breakdown |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
RSFR-(2X)125G dimensional specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Inner diameter | Wall thickness | ||||
| Φ0.6/0.40 | 0.90±0.20 | ≤0.40 | 0.33±0.10 | 200 | 0.4~0.7 |
| Φ0.8/0.50 | 1.10±0.20 | ≤0.50 | 0.33±0.10 | 200 | 0.6~0.8 |
| Φ1.0/0.65 | 1.50±0.20 | ≤0.65 | 0.36±0.10 | 200 | 0.75~0.9 |
| Φ1.5/0.85 | 2.00±0.20 | ≤0.85 | 0.36±0.10 | 200 | 0.95~1.4 |
| Φ2.0/1.00 | 2.50±0.20 | ≤1.00 | 0.45±0.10 | 200 | 1.1~1.8 |
| Φ2.5/1.30 | 3.00±0.20 | ≤1.30 | 0.45±0.10 | 200 | 1.35~2.3 |
| Φ3.0/1.50 | 3.50±0.20 | ≤1.50 | 0.45±0.10 | 200 | 1.6~2.7 |
| Φ3.5/1.80 | 4.00±0.20 | ≤1.80 | 0.45±0.10 | 200 | 1.85~3.2 |
| Φ4.0/2.00 | 4.70±0.20 | ≤2.00 | 0.45±0.10 | 200 | 2.1~3.6 |
| Φ4.5/2.30 | 5.00±0.20 | ≤2.30 | 0.56±0.10 | 100 | 2.35~4.0 |
| Φ5.0/2.50 | 5.50±0.20 | ≤2.50 | 0.56±0.10 | 100 | 2.6~4.5 |
| Φ6.0/3.00 | 6.50±0.20 | ≤3.00 | 0.56±0.10 | 100 | 3.1~5.4 |
| Φ7.0/3.50 | 7.50±0.30 | ≤3.50 | 0.56±0.10 | 100 | 3.7~6.3 |
| Φ8.0/4.00 | 8.50±0.30 | ≤4.00 | 0.56±0.10 | 100 | 4.2~7.2 |
| Φ9.0/4.50 | 9.50±0.30 | ≤4.50 | 0.56±0.10 | 100 | 4.7~8.0 |
| Φ10/5.00 | 10.50±0.30 | ≤5.00 | 0.56±0.10 | 100 | 5.2~9.0 |
| Φ11/5.50 | 11.50±0.30 | ≤5.50 | 0.56±0.10 | 100 | 5.7~10 |
| Φ12/6.00 | 12.50±0.30 | ≤6.00 | 0.56±0.10 | 100 | 6.2~11 |
| Φ13/6.50 | 13.50±0.30 | ≤6.50 | 0.56±0.10 | 100 | 6.7~12 |
| Φ14/7.00 | 14.50±0.30 | ≤7.00 | 0.70±0.10 | 100 | 7.3~13 |
| Φ15/7.50 | 15.50±0.40 | ≤7.50 | 0.70±0.10 | 100 | 7.8~14 |
| Φ16/8.00 | 16.50±0.40 | ≤8.00 | 0.70±0.10 | 100 | 8.3~15 |
| Φ17/8.50 | 17.50±0.40 | ≤8.50 | 0.70±0.10 | 100 | 8.8~16 |
| Φ18/9.00 | 19.00±0.50 | ≤9.00 | 0.70±0.10 | 100 | 9.3~17 |
| Φ20/10.0 | 22.00±0.50 | ≤10.0 | 0.80±0.15 | 100 | 10.4~19 |
| Φ22/11.0 | 24.00±0.50 | ≤11.0 | 0.80±0.15 | 100 | 11.4~21 |
| Φ25/12.5 | 26.00±0.50 | ≤12.5 | 0.90±0.15 | 50 | 12.8~24 |
| Φ28/14.0 | 29.00±0.50 | ≤14.0 | 0.90±0.15 | 50 | 14.4~29 |
| Φ30/15.0 | 31.50±1.00 | ≤15.0 | 0.90±0.15 | 50 | 16~29 |
| Φ35/17.5 | 36.50±1.00 | ≤17.5 | 1.00±0.15 | 50 | 18~34 |
| Φ40/20.0 | 41.50±1.00 | ≤20.0 | 1.00±0.15 | 50 | 21~39 |
| Φ45/22.0 | 46.50±1.50 | ≤22.5 | 1.00±0.15 | 25 | 23.5~44 |
| Φ50/25.0 | ≥50 | ≤25.0 | 1.10±0.15 | 25 | 26~49 |
| Φ60/30.0 | ≥60 | ≤30.0 | 1.10±0.15 | 25 | 35~50 |
| Φ70/35.0 | ≥70 | ≤35.0 | 1.20±0.15 | 25 | 40~60 |
| Φ80/40.0 | ≥80 | ≤40.0 | 1.30±0.20 | 25 | 45~70 |
| Φ90/45.0 | ≥90 | ≤45.5 | 1.30±0.20 | 25 | 50~80 |
| Φ100/50.0 | ≥100 | ≤50.0 | 1.30±0.20 | 25 | 55~85 |
| Φ120/60.0 | ≥120 | ≤60.0 | 1.30±0.20 | 25 | 65~100 |
| Φ150/75.0 | ≥150 | ≤75.0 | 1.30±0.20 | 25 | 80~120 |
| Φ180/90.0 | ≥180 | ≤90.0 | 1.30±0.20 | 25 | 85~150 |
| Φ210/105.0 | ≥210 | ≤105.0 | 1.30±0.30 | 25 | 110~180 |
| Φ230/115.0 | ≥230 | ≤115.5 | 1.30±0.30 | 25 | 120~210 |
| Φ250/125.0 | ≥250 | ≤125.0 | 1.30±0.30 | 25 | 130~230 |
| Φ300/150.0 | ≥300 | ≤150.0 | 1.30±0.30 | 25 | 160~250 |
RSFR-(2X)125G(CB)Ultra-thin flame-retardant heat-shrink tubing125℃ ultra-thin-wall, flame-retardant series for electronics, communications and automotive component protection.
Product introduction
125°C ultra-thin-wall flame-retardant heat-shrink tubing. It is made from irradiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. Its main functions are wire-harness protection, electrical insulation of connectors, rust and corrosion protection of solder joints, and mechanical protection. The ultra-thin wall suits miniature electronic device protection and is widely used to protect electronics, communications equipment and automotive components.
Product features
- Applicable standard: UL224,CAN/CSA C22.2 NO198.1-99
- Shrink ratio:2:1
- Initial shrink temperature: ≥+70°C
- Full recovery temperature: ≥+110°C
- Operating temperature: -55°C〜+125°C
- Flame-retardant, environmentally friendly, fast shrinking
- Environmental standards:RoHS
- Standard colors: black, white, red, yellow, green, blue and other colors, ten international standard colors in total
RSFR-(2X)125G(CB) product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 158°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 158°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Flame retardancy | ASTM D 2671 Method C | VW-1 |
| Withstand voltage (rated voltage 300V) | UL 224 | 1500 V,1min: no breakdown |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
RSFR-(2X)125G(CB) dimensional specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Inner diameter | Wall thickness | ||||
| Φ1.0CB | 1.40±0.20 | ≤0.65 | 0.20±0.10 | 200 | 0.7~1.0 |
| Φ1.5CB | 1.90±0.20 | ≤0.85 | 0.20±0.10 | 200 | 0.9~1.4 |
| Φ2.0CB | 2.40±0.20 | ≤1.00 | 0.22±0.10 | 200 | 1.1~1.8 |
| Φ2.5CB | 2.90±0.20 | ≤1.30 | 0.25±0.10 | 200 | 1.4~2.3 |
| Φ3.0CB | 3.40±0.20 | ≤1.50 | 0.28±0.10 | 200 | 1.6~2.7 |
| Φ3.5CB | 3.90±0.20 | ≤1.80 | 0.28±0.10 | 200 | 1.9~3.2 |
| Φ4.0CB | 4.40±0.20 | ≤2.00 | 0.30±0.10 | 200 | 2.1~3.6 |
| Φ4.5CB | 4.90±0.20 | ≤2.30 | 0.30±0.10 | 100 | 2.4~4.0 |
| Φ5.0CB | 5.50±0.20 | ≤2.50 | 0.32±0.10 | 100 | 2.6~4.5 |
| Φ6.0CB | 6.50±0.20 | ≤3.00 | 0.32±0.10 | 100 | 3.1~5.4 |
| Φ7.0CB | 7.50±0.30 | ≤3.50 | 0.32±0.10 | 200 | 3.7~6.3 |
| Φ8.0CB | 8.50±0.30 | ≤4.00 | 0.32±0.10 | 200 | 4.2~7.2 |
| Φ9.0CB | 9.50±0.30 | ≤4.50 | 0.35±0.10 | 200 | 4.7~8.0 |
| Φ10CB | 10.50±0.30 | ≤5.00 | 0.35±0.10 | 200 | 5.2~9.0 |
| Φ11CB | 11.50±0.30 | ≤5.50 | 0.40±0.10 | 200 | 5.7~10.0 |
| Φ12CB | 12.50±0.30 | ≤6.00 | 0.40±0.10 | 200 | 6.2~11.0 |
| Φ13CB | 13.50±0.30 | ≤6.50 | 0.40±0.10 | 200 | 6.7~12.0 |
| Φ14CB | 14.50±0.30 | ≤7.00 | 0.40±0.10 | 200 | 7.3~13.0 |
| Φ15CB | 15.50±0.40 | ≤7.50 | 0.40±0.10 | 200 | 7.8~14.0 |
| Φ16CB | 16.50±0.40 | ≤8.00 | 0.40±0.10 | 200 | 8.3~15.8 |
| Φ17CB | 17.50±0.40 | ≤8.50 | 0.40±0.10 | 200 | 8.8~16.0 |
| Φ18CB | 18.50±0.50 | ≤9.00 | 0.42±0.10 | 200 | 9.3~17.0 |
| Φ20CB | 20.50±0.50 | ≤10.00 | 0.45±0.10 | 200 | 10.5~19.0 |
| Φ22CB | 22.50±0.50 | ≤11.00 | 0.45±0.10 | 200 | 11.5~20.5 |
| Φ25CB | 25.50±0.50 | ≤12.50 | 0.45±0.10 | 100 | 13.0~24.0 |
| Φ28CB | 28.50±0.50 | ≤14.00 | 0.45±0.10 | 100 | 14.5~27.0 |
RSFR-(2X)135GMilitary-standard flame-retardant heat-shrink tubing2:1 shrink ratio; select to technical standards including AMS-DTL-23053/5.
Product introduction
Made from radiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. It protects harnesses, insulates connectors, prevents solder-joint rust and corrosion, and provides mechanical protection. The product meets military standards and is used in electronics, telecommunications, automotive component protection, ships and aircraft manufacturing.
Product features
- Applicable standard: AMS-DTL-23053/5, compatible with UL224, CAN/CSA C22.2 NO198.1-99
- Shrink ratio:2:1
- Initial shrink temperature: ≥+84°C
- Full recovery temperature: ≥+120°C
- Operating temperature: -55°C〜+135°C
- Good elasticity, flexible, flame retardant
- Environmental standards:RoHS
- Standard colors: black, white, red, yellow, green, blue and other colors, ten international standard colors in total (clear tubing is non-flame-retardant)
RSFR-(2X)135G product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 175°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 175°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Flame retardancy | ASTM D 2671 Method C | VW-1 |
| Withstand voltage (rated voltage 600V) | UL 224 | 2500V,1min: no breakdown |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥19.7 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
- Note: other sizes are manufactured to order.
RSFR-(2X)135G dimensional specifications
| Size mm | Dimensions before shrinkage mm — inner diameter | Fully recovered dimensions mm | Previous packaging m/reel | Application range mm | ||
|---|---|---|---|---|---|---|
| Maximum inner diameter | Wall thickness | |||||
| 3/64 | Φ1.0 | ≥1.20 | ≤0.60 | 0.41±0.10 | 200 | 0.70〜0.95 |
| 1/16 | Φ1.5 | ≥1.60 | ≤0.80 | 0.41±0.10 | 200 | 0.95〜1.25 |
| 3/32 | Φ2.0 | ≥2.40 | ≤1.20 | 0.51±0.10 | 200 | 1.35〜1.90 |
| 1/8 | Φ3.0 | ≥3.20 | ≤1.60 | 0.51±0.10 | 200 | 1.80〜2.55 |
| 3/16 | Φ4.5 | ≥4.80 | ≤2.40 | 0.51±0.10 | 100 | 2.65〜3.80 |
| 1/4 | Φ6.0 | ≥6.40 | ≤3.20 | 0.64±0.10 | 100 | 3.55〜5.10 |
| 3/8 | Φ9.0 | ≥9.50 | ≤4.80 | 0.64±0.10 | 100 | 5.30〜7.60 |
| 1/2 | Φ12 | ≥12.70 | ≤6.40 | 0.64±0.10 | 100 | 7.10〜10.11 |
| 3/4 | Φ18 | ≥19.10 | ≤9.50 | 0.76±0.15 | 100 | 0.50〜15.21 |
| 1 | Φ25 | ≥25.40 | ≤12.70 | 0.89±0.15 | 50 | 4.00〜20.31 |
| 1-1/4 | Φ32 | ≥32.00 | ≤15.90 | 0.89±0.15 | 50 | 7.50〜25.62 |
| 1-/2 | Φ38 | ≥38.00 | ≤19.10 | 1.00±0.15 | 50 | 1.00〜30.42 |
| 2 | Φ50 | ≥51.00 | ≤25.40 | 1.15±0.15 | 25 | 8.00〜40.84 |
| 3 | Φ75 | ≥76.00 | ≤38.10 | 1.27±0.20 | 25 | 2.00〜60.85 |
| 4 | Φ100 | ≥102.00 | ≤50.80 | 1.40±0.20 | 25 | 6.00〜81.60 |
| 5 | Φ120 | ≥125.00 | ≤63.50 | 1.40±0.25 | 25 | 70.00〜100.00 |
- Note: other sizes are manufactured to order.
- Note: other sizes are manufactured to order.
RSFR-(3X,4X)135G3:1 and 4:1 flame-retardant heat-shrink tubing to military standardsHigh shrink ratios of 3:1 and 4:1 for protecting connectors and transitions between different diameters.
Product introduction
3:1&4:1 flame-retardant heat-shrink tubing to military standards. It is made from irradiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. Its main functions are wire-harness protection, electrical insulation of connectors, rust and corrosion protection of solder joints, and mechanical protection. It meets US military standards. Its high shrink ratio accommodates components with varying diameters and it is widely used in electronics, communications, automotive component protection, shipbuilding and aircraft manufacturing.
Product features
- Applicable standard: AMS-DTL-23053/5, compatible with UL224, CAN/CSA C22.2 NO198.1-99
- Shrink ratio:3:1, 4:1
- Initial shrink temperature: ≥+84°C
- Full recovery temperature: ≥+120°C
- Operating temperature: -55°C〜+135°C
- Good elasticity, flexible, flame retardant
- Environmental standards:RoHS
- Standard colors: black, white, red, yellow, green, blue and other colors, ten international standard colors in total (clear tubing is non-flame-retardant)
RSFR-(3X,4X)135G product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 175°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 175°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Flame retardancy | ASTM D 2671 Method C | VW-1 |
| Withstand voltage (rated voltage 600V) | UL 224 | 2500 V,1min: no breakdown |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥19.7 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
- Note: other sizes can be customized.
RSFR-(3X,4X)135G dimensional specifications · 3:1
| Size mm | Inner diameter before shrinkage mm | Fully recovered dimensions mm | Previous packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Maximum inner diameter | Wall thickness | ||||
| Φ1.5/0.5 | ≥1.50 | ≤0.5 | 0.45±0.10 | 200 | 0.70〜1.20 |
| Φ3.0/1.0 | ≥3.00 | ≤1.0 | 0.55±0.10 | 200 | 1.20〜2.40 |
| Φ4.5/1.5 | ≥4.50 | ≤1.5 | 0.60±0.10 | 100 | 1.70〜3.60 |
| Φ6.0/2.0 | ≥6.00 | ≤2.0 | 0.65±0.10 | 100 | 2.20〜4.80 |
| Φ9/3.0 | ≥9.00 | ≤3.0 | 0.75±0.15 | 100 | 3.30〜7.20 |
| Φ12/4.0 | ≥12.00 | ≤4.0 | 0.75±0.15 | 100 | 4.40〜9.60 |
| Φ15/5.0 | ≥15.00 | ≤5.0 | 0.80±0.15 | 100 | 5.50〜12.00 |
| Φ18/6.0 | ≥18.00 | ≤6.0 | 0.85±0.15 | 100 | 6.60〜14.40 |
| Φ24/8.0 | ≥24.00 | ≤8.0 | 1.00±0.20 | 50 | 8.80〜19.20 |
| Φ30/10.0 | ≥30.00 | ≤10.0 | 1.15±0.20 | 50 | 11.0〜24.00 |
| Φ39/13.0 | ≥39.00 | ≤13.0 | 1.50±0.20 | 50 | 14.5〜31.20 |
| Φ50/16.0 | ≥50.00 | ≤16.0 | 2.60±0.20 | 25 | 18.0〜40.00 |
| Φ60/20.0 | ≥60.00 | ≤20.0 | 2.60±0.30 | 25 | 22.0〜48.00 |
| Φ70/23.0 | ≥70.00 | ≤23.0 | 2.60±0.30 | 25 | 25.5〜56.00 |
| Φ80/26.0 | ≥80.00 | ≤26.0 | 2.60±0.30 | 25 | 29.0〜64.00 |
| Φ90/30.0 | ≥90.00 | ≤30.0 | 2.70±0.30 | 25 | 33.0〜72.00 |
| Φ100/33.0 | ≥100.00 | ≤33.0 | 2.70±0.30 | 25 | 36.5〜80.00 |
- Note: other sizes can be customized.
RSFR-(3X,4X)135G dimensional specifications · 4:1
| Size mm | Inner diameter before shrinkage mm | Fully recovered dimensions mm | Standard packaging m/reel | |
|---|---|---|---|---|
| Maximum inner diameter | Total wall thickness W2 | |||
| φ3.2/0.8 | ≥3.2 | ≤0.8 | 0.60±0.20 | 100 |
| Φ4.0/1.0 | ≥4.0 | ≤1.0 | 0.70±0.20 | 100 |
| Φ6.0/1.5 | ≥6.0 | ≤1.5 | 0.78±0.25 | 100 |
| Φ8.0/2.0 | ≥8.0 | ≤2.0 | 0.80±0.25 | 100 |
| Φ10.0/2.5 | ≥10.0 | ≤2.5 | 0.85±0.25 | 100 |
| Φ12.0/3.0 | ≥12.0 | ≤3.0 | 0.90±0.30 | 100 |
| Φ16.0/4.0 | ≥16.0 | ≤4.0 | 1.00±0.30 | 100 |
| φ19.1/4.6 | ≥19.1 | ≤4.6 | 1.20±0.30 | 50 |
| Φ24.0/6.0 | ≥24.0 | ≤6.0 | 1.25±0.30 | 50 |
| φ25.4/6.5 | ≥25.4 | ≤6.5 | 1.25±0.30 | 50 |
| Φ30.0/7.5 | ≥30.0 | ≤7.5 | 1.25±0.30 | 50 |
| Φ32.0/8.0 | ≥32.0 | ≤8.0 | 1.25±0.30 | 50 |
| φ38.1/9.5 | ≥38.1 | ≤9.5 | 1.30±0.30 | 50 |
| Φ51.0/13.0 | ≥51.0 | ≤13.0 | 1.35±0.30 | 50 |
| Φ64.0/16.0 | ≥64.0 | ≤16.0 | 1.45±0.40 | 25 |
| Φ76.0/19.0 | ≥76.0 | ≤19.0 | 1.45±0.40 | 25 |
| Φ95.0/24.0 | ≥95.0 | ≤24.0 | 1.45±0.40 | 25 |
| Φ100.0/25.0 | ≥100.0 | ≤25.0 | 1.45±0.40 | 25 |
| Φ115.0/29.0 | ≥115.0 | ≤29.0 | 1.50±0.40 | 25 |
| Φ127.0/32.0 | ≥127.0 | ≤32.0 | 1.60±0.40 | 25 |
| Φ150.0/38.0 | ≥150.0 | ≤38.0 | 1.60±0.40 | 25 |
- Note: other sizes can be customized.
- Note: other sizes can be customized.
RSFR-(2X)150GHigh-temperature flame-retardant heat-shrink tubingOperating temperature up to 150℃, for wire harness and device protection in high-temperature conditions.
Product introduction
Made from radiation-crosslinked polyolefin, this high-temperature flame-retardant heat-shrink tubing has excellent physical, chemical and electrical properties. It protects wire harnesses, electrically insulates connectors, prevents solder-joint rust and corrosion, and provides mechanical protection. Its heat resistance and flame retardancy suit harnesses and devices in high-temperature environments, including electronics, telecommunications and automotive applications.
Product features
- Applicable standard: UL high-temperature tubing category, compatible with AMS-DTL-23053/5 and UL224, CAN/CSA C22.2 NO198.1-99
- Shrink ratio:2:1
- Initial shrink temperature: ≥+84°C
- Full recovery temperature: ≥+135°C
- Operating temperature: -55°C〜+150°C
- Flexible, flame-retardant
- Environmental standards:RoHS
- Standard colors: black, white, red, yellow, green, blue and other colors, ten international standard colors in total
RSFR-(2X)150G product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 180°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 180°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Flame retardancy | ASTM D 2671 Method C | VW-1 |
| Withstand voltage (rated voltage 600V) | UL 224 | 2500 V,1min: no breakdown |
| Thermal shock | UL224(250°CX4h) | No cracking or dripping |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
RSFR-(2X)150G dimensional specifications
| Size mm | Dimensions before shrinkage mm — inner diameter | Fully recovered dimensions mm | Standard packaging m/reel | Application range mm | |
|---|---|---|---|---|---|
| Maximum inner diameter | Wall thickness | ||||
| Φ1.0 | 1.5±0.2 | ≤0.65 | 0.38±0.10 | 200 | 0.75〜1.00 |
| Φ1.5 | 2.0±0.2 | ≤0.85 | 0.40±0.10 | 200 | 0.95〜1.40 |
| Φ2.0 | 2.5±0.2 | ≤1.00 | 0.44±0.10 | 200 | 1.10〜1.80 |
| Φ2.5 | 3.0±0.2 | ≤1.25 | 0.44±0.10 | 200 | 1.40〜2.20 |
| Φ3.0 | 3.5±0.2 | ≤1.50 | 0.44±0.10 | 200 | 1.65〜2.60 |
| Φ3.5 | 4.0±0.2 | ≤1.75 | 0.44±0.10 | 200 | 1.95〜3.00 |
| Φ4.0 | 4.5±0.2 | ≤2.00 | 0.44±0.10 | 200 | 2.20〜3.40 |
| Φ4.5 | 5.0±0.2 | ≤2.25 | 0.44±0.10 | 100 | 2.50〜3.80 |
| Φ5.0 | 5.5±0.2 | ≤2.50 | 0.56±0.10 | 100 | 2.80〜4.20 |
| Φ6.0 | 6.5±0.2 | ≤3.00 | 0.56±0.10 | 100 | 3.30〜5.00 |
| Φ7.0 | 7.5±0.3 | ≤3.50 | 0.56±0.15 | 100 | 3.90〜5.75 |
| Φ8.0 | 8.5±0.3 | ≤4.00 | 0.56±0.15 | 100 | 4.40〜6.50 |
| Φ9.0 | 9.5±0.3 | ≤4.50 | 0.56±0.15 | 100 | 5.00〜7.30 |
| Φ10.0 | 10.5±0.3 | ≤5.00 | 0.56±0.15 | 100 | 5.50〜8.10 |
| Φ11.0 | 11.5±0.3 | ≤5.50 | 0.56±0.15 | 100 | 6.10〜8.90 |
| Φ12.0 | 12.5±0.4 | ≤6.00 | 0.56±0.15 | 100 | 6.60〜9.60 |
| Φ13.0 | 13.5±0.4 | ≤6.50 | 0.69±0.15 | 100 | 7.20〜10.40 |
| Φ14.0 | 14.5±0.4 | ≤7.00 | 0.69±0.15 | 100 | 7.70〜11.20 |
| Φ15.0 | 15.5±0.4 | ≤7.50 | 0.69±0.15 | 100 | 8.30〜12.00 |
| Φ16.0 | 16.5±0.4 | ≤8.00 | 0.69±0.15 | 100 | 8.80〜12.80 |
| Φ17.0 | 17.5±0.4 | ≤8.50 | 0.69±0.15 | 100 | 9.40〜13.60 |
| Φ18.0 | 19.2±0.5 | ≤9.00 | 0.77±0.15 | 100 | 9.90〜14.90 |
| Φ20.0 | 22.0±0.5 | ≤10.0 | 0.77±0.15 | 100 | 11.0〜17.20 |
| Φ22.0 | 24.0±0.6 | ≤11.00 | 0.77±0.15 | 100 | 12.1〜18.70 |
| Φ25.0 | 26.0±0.6 | ≤12.50 | 0.87±0.20 | 50 | 13.8〜20.30 |
| Φ28.0 | 29.0±0.6 | ≤14.00 | 0.87±0.20 | 50 | 15.4〜22.70 |
| Φ30.0 | 31.5±1.5 | ≤15.00 | 0.87±0.20 | 50 | 16.5〜24.00 |
| Φ35.0 | 36.5±1.5 | ≤17.50 | 0.87±0.20 | 50 | 19.3〜28.00 |
| Φ40.0 | 41.5±1.5 | ≤20.00 | 0.87±0.20 | 50 | 22.0〜32.00 |
| Φ50.0 | 51.5±1.5 | ≤25.00 | 0.97±0.20 | 25 | 28.0〜40.00 |
| Φ60.0 | ≥60.0 | ≤30.00 | 1.10±0.20 | 25 | 33.0〜48.00 |
| Φ70.0 | ≥70.0 | ≤35.00 | 1.20±0.20 | 25 | 39.0〜56.00 |
| Φ80.0 | ≥80.0 | ≤40.00 | 1.30±0.20 | 25 | 44.0〜64.00 |
| Φ100.0 | ≥100.0 | ≤50.00 | 1.30±0.20 | 25 | 55.0〜80.00 |
| Φ120.0 | ≥120.0 | ≤60.00 | 1.30±0.20 | 25 | 66.0〜96.00 |
| Φ150.0 | ≥150.0 | ≤75.00 | 1.30±0.20 | 25 | 83.0〜120.00 |
RSFR-(2X,3X)125YG2:1 and 3:1 yellow/green identification heat-shrink tubingYellow/green grounding identification tubing, available with 2:1 and 3:1 shrink ratios.
Product introduction
Yellow/green heat-shrink tubing is made by two-color co-extrusion of environmentally friendly polyolefin followed by irradiation modification. It is flexible and flame-retardant, with bright, durable colors and stable performance. Its alternating yellow/green appearance identifies grounding conductors in harnesses and cables, special cables, busbars and pipes.
Product features
- Shrink ratio:2:1, 3:1
- Initial shrink temperature: ≥+70°C
- Full recovery temperature: ≥+125°C
- Operating temperature: -55°C〜+125°C
- Flexible, flame-retardant
- Environmental standards:RoHS
- Standard color: alternating yellow/green
RSFR-(2X,3X)125YG dimensional specifications · 2:1
| Size mm | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | |
|---|---|---|---|---|
| Inner diameter | Wall thickness | |||
| Φ1.0 | 1.50±0.30 | ≤0.7 | 0.28±0.10 | 200 |
| Φ1.5 | 2.00±0.30 | ≤0.9 | 0.30±0.10 | 200 |
| Φ2.0 | 2.50±0.30 | ≤1.0 | 0.35±0.10 | 200 |
| Φ2.5 | 3.00±0.30 | ≤1.3 | 0.36±0.10 | 200 |
| Φ3.0 | 3.50±0.40 | ≤1.5 | 0.38±0.10 | 200 |
| Φ3.5 | 4.00±0.40 | ≤1.8 | 0.40±0.10 | 200 |
| Φ4.0 | 4.50±0.40 | ≤2.0 | 0.45±0.10 | 200 |
| Φ4.5 | 5.00±0.40 | ≤2.3 | 0.45±0.10 | 100 |
| Φ5.0 | 5.50±0.40 | ≤2.5 | 0.45±0.10 | 100 |
| Φ6.0 | 6.50±0.40 | ≤3.0 | 0.50±0.10 | 100 |
| Φ7.0 | 7.50±0.40 | ≤3.5 | 0.50±0.10 | 100 |
| Φ8.0 | 8.50±0.50 | ≤4.0 | 0.55±0.10 | 100 |
| Φ9.0 | 9.50±0.50 | ≤4.5 | 0.55±0.10 | 100 |
| Φ10.0 | 10.50±0.50 | ≤5.0 | 0.55±0.10 | 100 |
| Φ11.0 | 11.50±0.50 | ≤5.5 | 0.60±0.10 | 100 |
| Φ12.0 | 12.50±0.50 | ≤6.0 | 0.60±0.10 | 100 |
| Φ13.0 | 13.50±0.50 | ≤6.5 | 0.60±0.10 | 100 |
| Φ14.0 | 14.50±0.50 | ≤7.0 | 0.65±0.10 | 100 |
| Φ15.0 | 15.50±0.60 | ≤7.5 | 0.70±0.10 | 100 |
| Φ16.0 | 17.00±0.60 | ≤8.0 | 0.70±0.10 | 100 |
| Φ17.0 | 17.50±0.60 | ≤8.5 | 0.70±0.10 | 100 |
| Φ18.0 | 19.00±0.70 | ≤9.0 | 0.70±0.15 | 100 |
| Φ20,0 | 22.00±0.70 | ≤10.0 | 0.80±0.15 | 100 |
| Φ22.0 | 24.00±0.70 | ≤11.0 | 0.90±0.15 | 100 |
| Φ25.0 | 26.00±0.70 | ≤12.5 | 0.90±0.15 | 50 |
| Φ28.0 | 29.00±0.70 | ≤14.0 | 0.95±0.15 | 50 |
| Φ30.0 | 31.50±0.70 | ≤15.0 | 0.95±0.15 | 50 |
| Φ35.0 | 36.50±0.70 | ≤17.5 | 1.00±0.20 | 50 |
| Φ40.0 | 41.50±0.70 | ≤20.0 | 1.00±0.20 | 50 |
| Φ45.0 | 46.00±0.70 | ≤22.5 | 1.00±0.20 | 25 |
| Φ50.0 | 51.00±0.70 | ≤25.0 | 1.00±0.20 | 25 |
| Φ60.0 | ≥60.0 | ≤30.0 | 1.10±0.20 | 25 |
| Φ70.0 | ≥70.0 | ≤35.0 | 1.20±0.20 | 25 |
| Φ80.0 | ≥80.0 | ≤40.0 | 1.30±0.20 | 25 |
| Φ90.0 | ≥90.0 | ≤45.0 | 1.50±0.20 | 25 |
| Φ100.0 | ≥100.0 | ≤50.0 | 1.65±0.20 | 25 |
| Φ120.0 | ≥120.0 | ≤60.0 | 1.70±0.20 | 15 |
| Φ150.0 | ≥150.0 | ≤75.0 | 1.70±0.20 | 15 |
| Φ180.0 | ≥180.0 | ≤90.0 | 1.75±0.20 | 15 |
RSFR-(2X,3X)125YG product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 158°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 158°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -8〜+8 |
| Flame retardancy | ASTM D 2671 Method C | VW-1 |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
RSFR-(2X,3X)125YG dimensional specifications · 3:1
| Size mm | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | |
|---|---|---|---|---|
| Inner diameter | Wall thickness | |||
| Φ3.2 | ≥3.2 | ≤1.0 | 0.55±0.15 | 200 |
| Φ4.8 | ≥4.8 | ≤1.5 | 0.60±0.15 | 100 |
| Φ6.4 | ≥6.4 | ≤2.0 | 0.65±0.15 | 100 |
| Φ9.5 | ≥9.5 | ≤3.0 | 0.75±0.15 | 50 |
| Φ12.7 | ≥12.7 | ≤4.0 | 0.75±0.20 | 50 |
| Φ19.1 | ≥19.1 | ≤6.0 | 0.85±0.20 | 50 |
| Φ25.4 | ≥25.4 | ≤8.0 | 1.00±0.20 | 50 |
| Φ39.0 | ≥39.0 | ≤13.0 | 1.50±0.20 | 50 |
RSFR-(2X)125HLS90℃ halogen-free, environmentally conscious low-temperature heat-shrink tubingFull recovery temperature ≥90℃, for devices and wire harnesses requiring a lower installation temperature.
Product introduction
Halogen-free low-temperature heat-shrinkable tubing is made from irradiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. Designed for harness and electronic-component protection requiring low-temperature shrinking, it reduces heat exposure during installation and is widely used in electronics and communications.
Product features
- Applicable standard: UL224 CAN/CSA C22.2 NO198.1-99
- Shrink ratio:2:1
- Initial shrink temperature: ≥+70°C
- Full recovery temperature: ≥+90°C
- Operating temperature: -55°C〜+125°C
- Halogen-free, low-smoke, non-toxic, flexible
- Environmental standards:RoHS, IPC/JEDEC-J-STD-709; class H materials
- Standard colors: black, white, red, yellow, green, blue and other colors, ten international standard colors in total
RSFR-(2X)125HLS product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 158°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 158°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Cold-bend resistance | -30°CX1h | No cracking |
| Dielectric strength (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
- Note: * sizes are nonstandard tubing, manufactured to order.
RSFR-(2X)125HLS dimensional specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | |
|---|---|---|---|---|
| Inner diameter | Wall thickness | |||
| *Φ1.0 | 1.50±0.20 | ≤0.65 | 0.36±0.10 | 200 |
| *Φ1.5 | 2.00±0.20 | ≤0.85 | 0.36±0.10 | 200 |
| *Φ2.0 | 2.50±0.20 | ≤1.00 | 0.45±0.10 | 200 |
| *Φ2.5 | 3.00±0.20 | ≤1.30 | 0.45±0.10 | 200 |
| *Φ3.0 | 3.50±0.20 | ≤1.50 | 0.45±0.10 | 200 |
| *Φ3.5 | 4.00±0.20 | ≤1.80 | 0.45±0.10 | 200 |
| *Φ4.0 | 4.50±0.20 | ≤2.00 | 0.45±0.10 | 200 |
| *Φ4.5 | 5.00±0.20 | ≤2.30 | 0.56±0.10 | 100 |
| *Φ5.0 | 5.50±0.20 | ≤2.50 | 0.56±0.10 | 100 |
| *Φ5.5 | 6.00±0.20 | ≤2.75 | 0.56±0.10 | 100 |
| *Φ6.0 | 6.50±0.20 | ≤3.00 | 0.56±0.10 | 100 |
| *Φ7.0 | 7.50±0.30 | ≤3.50 | 0.56±0.10 | 100 |
| *Φ8.0 | 8.50±0.30 | ≤4.00 | 0.56±0.10 | 100 |
| *Φ9.0 | 9.50±0.30 | ≤4.50 | 0.56±0.10 | 100 |
| *Φ10 | 10.50±0.30 | ≤5.00 | 0.56±0.10 | 100 |
| *Φ11 | 11.50±0.30 | ≤5.50 | 0.56±0.10 | 100 |
| *Φ12 | 12.50±0.30 | ≤6.00 | 0.56±0.10 | 100 |
| *Φ14 | 14.50±0.30 | ≤7.00 | 0.69±0.10 | 100 |
| *Φ15 | 15.50±0.40 | ≤7.50 | 0.69±0.10 | 100 |
| *Φ16 | 16.50±0.40 | ≤8.00 | 0.69±0.10 | 100 |
| *Φ18 | 19.00±0.50 | ≤9.00 | 0.69±0.15 | 100 |
| *Φ20 | 22.00±0.50 | ≤10.0 | 0.83±0.15 | 100 |
| *Φ22 | 24.00±0.50 | ≤11.0 | 0.83±0.15 | 100 |
| *Φ25 | 26.00±0.50 | ≤12.5 | 0.89±0.15 | 50 |
| *Φ28 | 29.00±0.50 | ≤14.0 | 0.89±0.15 | 50 |
| *Φ30 | 31.50±1.00 | ≤15.0 | 1.00±0.15 | 50 |
| *Φ35 | 36.50±1.00 | ≤17.5 | 1.00±0.15 | 50 |
| *Φ40 | 41.50±1.00 | ≤20.0 | 1.00±0.15 | 50 |
| *Φ45 | 46.50±1.00 | ≤22.5 | 1.00±0.15 | 25 |
| *Φ50 | ≥50.0 | ≤25.0 | 1.10±0.15 | 25 |
- Note: * sizes are nonstandard tubing, manufactured to order.
- Note: * sizes are nonstandard tubing, manufactured to order.
RSFR-(2X)125HECHalogen-Free Flame-Retardant Polyolefin Heat-Shrinkable Tubing for Batteries and CapacitorsFor external sleeving of batteries and capacitors: thin walls and high rigidity for easy insertion.
Product introduction
Halogen-free flame-retardant tubing for batteries and capacitors is made from irradiation-crosslinked polyolefin with excellent physical, chemical and electrical properties. Its ultra-thin wall and high hardness facilitate insertion. Mainly used for battery and capacitor insulation and protection, it can fully replace PVC and PET tubing.
Product features
- Shrink ratio:2:1
- Initial shrink temperature: ≥+70°C
- Full recovery temperature: ≥+120°C
- Operating temperature: -55°C〜+125°C
- Halogen-free, flame-retardant, low-smoke, non-toxic, thin-wall, fast-shrinking
- Environmental standards:RoHS, SONY
- Standard color: black (other colors on request)
RSFR-(2X)125HEC product data
| Performance | Test method | Parameter |
|---|---|---|
| Tensile strength (MPa) | ASTM D 2671 | ≥10.4 |
| Elongation at break (%) | ASTM D 2671 | ≥200 |
| Tensile strength after aging (MPa) | 158°CX168h | ≥7.3 |
| Elongation at break after aging (%) | 158°CX168h | ≥100 |
| Longitudinal change (%) | ASTM D 2671 | -5〜+5 |
| Flame retardancy | ASTM D 2671 Method B | VW-1 |
| Dielectric withstand voltage (600V) | UL 224 | 2500V,1min: no breakdown |
| Dielectric strength (alternative to withstand voltage) (kV/mm) | ASTM D 149 | ≥15 |
| Volume resistivity (Ω·cm) | IEC 60093 | ≥10¹⁴ |
- Note: full recovery conditions are 200°C, 3min.
RSFR-(2X)125HEC dimensional specifications
| Specifications | Supplied inner diameter mm | Fully recovered dimensions mm | Standard packaging m/reel | |
|---|---|---|---|---|
| Inner diameter | Wall thickness | |||
| Φ5.0 | 5.50±0.20 | ≤2.5 | 0.32±0.10 | 100 |
| Φ6.0 | 6.50±0.20 | ≤3.0 | 0.32±0.10 | 100 |
| Φ8 | 8.50±0.30 | ≤4.0 | 0.32±0.10 | 100 |
| Φ10 | 10.50±0.30 | ≤5.0 | 0.35±0.10 | 100 |
| Φ12 | 12.50±0.30 | ≤6.0 | 0.35±0.10 | 100 |
| Φ14 | 14.50±0.30 | ≤7.0 | 0.36±0.10 | 100 |
| Φ16 | 12.50±0.30 | ≤8.0 | 0.36±0.10 | 100 |
| Φ18 | 18.50±0.30 | ≤9.0 | 0.36±0.10 | 100 |
| Φ20 | 20.50±0.40 | ≤10.0 | 0.40±0.10 | 100 |
| Φ22 | 22.50±0.40 | ≤11.0 | 0.40±0.10 | 100 |
| Φ25 | 25.60±0.40 | ≤12.5 | 0.40±0.10 | 50 |
| Φ30 | 31.30±0.80 | ≤17.6 | 0.43±0.10 | 50 |
| Φ35 | 36.30±0.80 | ≤20.5 | 0.48±0.10 | 50 |
| Φ40 | 41.30±0.80 | ≤23.5 | 0.65±0.10 | 50 |
| Φ45 | 46.30±0.80 | ≤26.4 | 0.65±0.10 | 25 |
| Φ50 | 51.30±0.80 | ≤29.4 | 0.65±0.10 | 25 |
| Φ55 | 56.50±1.00 | ≤32.3 | 0.65±0.10 | 25 |
| Φ60 | 61.50±1.00 | ≤35.2 | 0.65±0.10 | 25 |
| Φ65 | 66.50±1.00 | ≤38.2 | 0.72±0.15 | 25 |
| Φ70 | 71.50±1.00 | ≤41.1 | 0.72±0.15 | 25 |
| Φ75 | 76.50±1.00 | ≤44.1 | 0.72±0.15 | 25 |
| Φ80 | 81.50±1.50 | ≤47.0 | 0.72±0.15 | 25 |
| Φ85 | 86.50±1.50 | ≤50.0 | 0.74±0.15 | 25 |
| Φ90 | 92.00±1.50 | ≤52.9 | 0.74±0.15 | 25 |
| Φ100 | 102.00±2.00 | ≤58.8 | 0.74±0.20 | 25 |
- Note: full recovery conditions are 200°C, 3min.
- Note: full recovery conditions are 200°C, 3min.
Specification confirmation and product matching
Match the tubing to the item being covered.
Please provide: product series, dimensions of the item to be sleeved, working temperature, shrink ratio, color, flame-retardancy or environmental requirements, quantity and packaging.
Send inquiry →